Comparison of flat and hollow-fiber mixed-matrix composite membranes for CO2 separation with temperature
Zeolite A/poly (1-trimethylsilyl-1-propyne) (zeoliteA/PTMSP) and [emim][Ac]/chitosan (IL/CS) are mixed-matrix membrane (MMM) materials with enhanced CO2/N2 permselectivity even at higher temperature. The scalability to asymmetric flat and hollow-fiber geometry by a simple dip-coating method was anal...
| Autores: | , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2017 |
| País: | España |
| Institución: | Universidad de Cantabria (UC) |
| Repositorio: | UCrea Repositorio Abierto de la Universidad de Cantabria |
| Idioma: | inglés |
| OAI Identifier: | oai:repositorio.unican.es:10902/13043 |
| Acceso en línea: | http://hdl.handle.net/10902/13043 |
| Access Level: | acceso abierto |
| Palabra clave: | CO2 capture High permeance Mixed-matrix composite membranes Post-combustion capture |
| Sumario: | Zeolite A/poly (1-trimethylsilyl-1-propyne) (zeoliteA/PTMSP) and [emim][Ac]/chitosan (IL/CS) are mixed-matrix membrane (MMM) materials with enhanced CO2/N2 permselectivity even at higher temperature. The scalability to asymmetric flat and hollow-fiber geometry by a simple dip-coating method was analyzed. The CO2/N2 separation performance was evaluated at different temperatures. The resulting composite membranes exhibit a significantly enhanced CO2permeation flux because the MMM layer thickness is reduced by 97?% from flat to hollow-fiber geometries in IL-CS composite membranes, while the selectivity is maintained similar to the self-standing membranes, thus proving that compatibility between the membrane component materials leads to a defect-free composite membrane, regardless the geometry and temperature. |
|---|